Role of Oxygen Vacancies in Stabilizing the Orthorhombic Phases of Hf0.5Zr0.5O2 Nanoparticles

In this work we study the stabilization of the orthorhombic phases in small Hf0.5Zr0.5O2 nanoparticles (average size ~ 7 nm) annealed under different oxygen partial pressures. Concentration of the oxygen vacancies, which is determined by annealing conditions, was estimated from the electron paramagnetic resonance spectra and X-ray photoelectron spectroscopy. The fraction of the orthorhombic phases, that is determined by the X-ray diffraction and nuclear magnetic resonance, depends on the concentration of oxygen vacancies. Phenomenological calculations based on Landau-Ginzburg-Devonshire theory considering trilinear coupling between nonpolar, antipolar and polar phonon modes, indicate that chemical strain induced by oxygen vacancies can stabilize the orthorhombic phase o-III with the ferroelectric long-range ordering in small Hf0.5Zr0.5O2 nanoparticles. The theory confirms the stability of ferroelectric polarization in the vacancy-enriched Hf0.5Zr0.5O2 nanoparticles. The increase in the intensity of the dielectric permittivity maximum, observed near 350 - 380 K in the PVDF matrix with the Hf0.5Zr0.5O2 nanoparticles annealed in the CO+CO2 atmosphere, is clearly associated with the increase in oxygen vacancies concentration. The vacancies lead to the defect-induced elastic dipole formation and to the increase in ionic conductivity, which decreases the depolarization field and may induce the ferroelectric-like phase transition in the vacancy-enriched Hf0.5Zr0.5O2 nanoparticles. Due to the interfacial effects the negative capacitance states may be realized in weakly screened and spatially isolated Hf0.5Zr0.5O2 nanoparticles embedded in the PVDF matrix.