Anomalous Subsurface Vacancy Stabilization Dictated by Geometry-Electronic Decoupling on Metal Surfaces

Vacancy formation energetics fundamentally govern the structural integrity and catalytic behavior of metal surfaces. Contrary to conventional coordination-dependent broken-bond models, we identify an anomalous thermodynamic inversion on close-packed surfaces across Ir, Pt, Au with face-centered cubic (FCC) lattice and Be, Zn, Cd with hexagonal close-packed (HCP) lattice, where subsurface vacancies are intrinsically more stable than surface ones. Using high-throughput DFT calculations and machine learning force fields, we demonstrate that the physical origins of this anomaly are fundamentally decoupled between the two crystal systems. For the FCC trio, pronounced surface relaxation and a profound real-space electronic localization induce directional, covalent-like intralayer bonding, materializing a "geometry-electronic decoupling" mechanism. Crucially, this unconventional thermodynamic hierarchy enables a dynamic "self-healing" mechanism on Pt(111) that preserves an intact topmost layer and prevents catalytic degradation during hydrogen evolution and oxygen reduction reactions. It also successfully decoding the critical defect threshold (~8%) for lifting the Au(100) surface reconstruction. Our work challenges classical scalar defect models and provides a fresh paradigm for engineering catalyst surface integrity.